Insights into Polymer Film Instability Could Aid High Tech Industries

For Immediate Release: January 13, 2009

*
Bookmark and Share

Contact: Chad Boutin
301-975-4261

crystallization

Crystallization (left) occurs as polymers harden into thin films, which are used widely in electronics technology. But when dewetting (right) also occurs, inhomogeneities in the film can degrade performance. NIST scientists found that temperature determines which process dominates film formation, and that keeping certain angles between crystallization fronts can largely prevent dewetting.

Credit: NIST
View hi-resolution image

While exploring the properties of polymer formation, a team of scientists at the National Institute for Standards and Technology (NIST) has made a fundamental discovery* about these materials that could improve methods of creating the stable crystalline films that are widely used in electronics applications—and also offer insight into a range of other phenomena.

The team has determined that temperature can play a decisive role in determining which of two competing processes—called crystallization and dewetting—will “take the lead” when a semicrystalline polymer film hardens, thereby granting qualitatively different properties to the finished film. The findings could lead to better control of these two processes, which can cause imperfections in polymer films during their formation.

Such imperfections can hinder the performance of potential new technologies, such as solar cells or thin film transistors, that employ organic polymer films on their surfaces, according to research chemist Christopher Soles. At this point, he said, the organic semiconductor industry is being hindered by a lack of understanding of crystal formation in thin polymer films.

“If organic photovoltaics—to take just one example—are ever to be realized and marketed, we need to understand how the film formation process works,” said Soles. “You have to know the properties of these materials first in order to control their stability.”

As a polymer film cools, two different things can happen locally within it: Either its molecules can crystallize, starting from some nucleation center (such as a scratch) and then expanding into the surrounding unstable film. Or, because of chemical differences between the polymer and its underlying substrate, such as a silicon wafer, the film’s molecules can “dewet”—similar to the beading up of water droplets on a windshield. If crystallization and dewetting occur simultaneously, they can couple to create imperfections that can be a nuisance for applications that rely on film uniformity, such as organic solar cells. The challenge is to bring these instabilities under control for constructive purposes.

Using model polymers with well understood crystallization behavior, the team discovered that a few degrees’ variation in temperature controls whether crystallization or dewetting will dominate the hardening process. They also found that when two growing crystals expand and collide, the stress created where they contact each other can cause dewetting—but if the angle between the two expansion fronts is small enough, then this localized dewetting might be averted.

“What’s cool about this discovery is not just that we have better understanding of polymer films, which are widely used in a range of coating and interface technologies,” said coauthor Jack Douglas, also of NIST’s polymers division. “There’s a whole class of mathematical problems in which you have multiple effects that are all fighting for domination of some field of action—the spreading of languages, for example, or the growth of different tissues within organisms. It’s a very common phenomenon, and this research could provide theoretical insight into those problems as well.”

Funding for this study was provided by the National Research Council.

* B.C. Okerberg, B.C. Berry, T.R. Garvey, J.F. Douglas, A. Karim and C.L. Soles. Competition between crystallization and dewetting fronts in this polymer films. Soft Matter, November 2008, 1-7. DOI: 10.1039/b806074f