In Situ Neutron Reflectometry Study of a Tungsten Oxide/Li-Ion Battery Electrolyte Interface

Published

January 18, 2023

Author(s)

Eric Rus, Joseph A. Dura

Abstract

The solid electrolyte interface/interphase (SEI) is of great importance to the viable operation of lithium ion batteries. In the present work the interface between a tungsten oxide electrode and an electrolyte solution consisting of LiPF₆ in a deuterated ethylene carbonate/diethyl carbonate solvent was characterized with in situ neutron reflectometry (NR) at a series of applied electrochemical potentials. NR data were fit to yield neutron scattering length density (SLD)-depth profiles in the surface normal direction, from which composition-depth profiles were inferred. The goals of this work were to characterize solid electrolyte interface formation on a model transition metal oxide, an example of a conversion electrode, to characterize the lithiation of WO₃, and to help interpret the results of an earlier study of tungsten electrodes without intentionally grown surface oxide. The WO₃ electrode was produced by thermal oxidation of a W thin film. Co-analysis of NR and x-ray reflectivity data indicated the stoichiometry of the thermal oxide was WO₃. As the electrode was polarized to progressively more reducing potentials, starting from open circuit and down to +0.25 V vs Li/Li⁺, the layer that was originally WO₃ expanded and increased in lithium content. The reduced electrode consisted of two to three layers: an inner layer (the evolving conversion electrode) which may have been mixed W and Li₂O and unreacted WO3, a layer rich in protons and/or lithium , possibly corresponding to LiOH or LiH (the inner SEI), and an outermost layer adjacent to the solution with an SLD close to that of the solution, possibly consisting of lower SLD species with solution-filled porosity or deuteron-rich species derived from the solvents (the outer SEI), though the presence of this layer was tenuous. For the steps in the direction of more oxidizing potentials, the evolution of the layer structure was qualitatively the reverse of that seen when stepping towards more negative potentials, though with hysteresis. The SLD gradient suggested the reaction was not limited by diffusion within the film.

Citation

ACS Applied Materials and Interfaces

Volume

15

Issue

2

Pub Type

Journals

Download Paper

DOI Link

Keywords

solid electrolyte interface, SEI, lithium, conversion electrode, Neutron Reflectometry, thin film

Citation

Rus, E. and Dura, J. (2023), In Situ Neutron Reflectometry Study of a Tungsten Oxide/Li-Ion Battery Electrolyte Interface, ACS Applied Materials and Interfaces, [online], https://dx.doi.org/10.1021/acsami.2c16737 (Accessed December 26, 2024)