Role of microstructure and composition in resisting hydrogen embrittlement of fastener grade steels, Corrosion Science
(Accessed March 17, 2025)
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
Secure .gov websites use HTTPS
A lock (
) or https:// means you’ve safely connected to the .gov website. Share sensitive information only on official, secure websites.
Role of microstructure and composition in resisting hydrogen embrittlement of fastener grade steels
Published
Author(s)
, Jack Grochowski, Lloyd Heldt, Karl Rundman
Abstract
The degree of hydrogen embrittlement for several fastener grade steels has been determined. The technique used to assess the resistance to hydrogen embrittlement of the steels was the rising step load test on notched tensile specimens. While microstructural alteration resulted in some improvement in resistance to hydrogen embrittlement, the overriding factor contributing to susceptibility of the steel was strength. The susceptibilities of the microstructures to hydrogen embrittlement, ranked in decreasing order, are as follows: tempered martensite, bainite, fine pearlite. The effect of alloying was also assessed by comparing rising step load results from different fastener grade steels with similar microstructures. In most cases, the alloy chemistry had little effect on rising step load results, presumably due to trap saturation associated with this testing technique.Citation
Corrosion Science
Volume
52
Pub Type
Journals
Keywords
steel, microstructure, hydrogen embrittlement, bainite, pearlite, tempered martensite07