Thermally Induced Stress Relaxation and Densification of Spin-on-Glass Thin Films, Applied Physics Letters, [online], https://tsapps.nist.gov/publication/get_pdf.cfm?pub_id=851605
(Accessed December 26, 2024)
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
Secure .gov websites use HTTPS
A lock (
) or https:// means you’ve safely connected to the .gov website. Share sensitive information only on official, secure websites.
Thermally Induced Stress Relaxation and Densification of Spin-on-Glass Thin Films
Published
Author(s)
, , , D Feiler, W. Xia
Abstract
The stress-temperature relationship of silica spin-on-glass thin films on silicon wafers was studied. Upon heating the stress-temperature curves showed a dramatically increasing slope when the temperature of the film was greater than 340 C. At 450 C, a significant, irreversible change in the stress of the film was observed. This change in stress was correlated with an increase in film electron density and a decrease in film thickness. This observed thermally activated stress-relaxation behavior was interpreted in terms of reflow of the glassy hydrogen-silsequioxane-based material.Citation
Applied Physics Letters
Volume
76
Issue
No. 4
Pub Type
Journals
Download Paper
Keywords
hydrogen-silsesquioxane, low-K dielectric, spin-on-glass, stress, thin-film
Citation
Issues
If you have any questions about this publication or are having problems accessing it, please contact reflib@nist.gov.
Created December 31, 1999, Updated October 12, 2021